S-Plastic Ultem 9070 High Flow Polyetherimide Blend

Product Categories
SAMTION INTERNATIONAL LIMITED
Contact Now

S-Plastic Ultem 9070 High Flow Polyetherimide Blend

  • 1
  • 2
  • 3

Brand Name : S-Plastic Ultem

Model Number : 9070

Certification : COA/ICP Test/Rohs/MSDS

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Flow Rate, 337°C/6.6 kgf : 11

Contact Now

S-Plastics Ultem 9070 resin is High flow Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming.

​Property

TYPICAL PROPERTIES (1)
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 5 mm/min 96 MPa ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min 70 % ASTM D 638
Tensile Modulus, 5 mm/min 3370 MPa ASTM D 638
Flexural Stress, yld, 2.6 mm/min, 100 mm span 137 MPa ASTM D 790
Flexural Modulus, 2.6 mm/min, 100 mm span 3170 MPa ASTM D 790
IMPACT Value Unit Standard
Izod Impact, notched, 23°C 85 J/m ASTM D 256
Izod Impact, Reverse Notched, 3.2 mm 1975 J/m ASTM D 256
Gardner, 23°C 23 J ASTM D 3029
THERMAL Value Unit Standard
HDT, 1.82 MPa, 6.4 mm, unannealed 196 °C ASTM D 648
PHYSICAL Value Unit Standard
Specific Gravity 1.3 - ASTM D 792
Mold Shrinkage, flow, 3.2 mm 0.5 - 0.7 % S-Plastics Method
Mold Shrinkage, xflow, 3.2 mm 0.5 - 0.7 % S-Plastics Method
Melt Flow Rate, 337°C/6.6 kgf 11 g/10 min ASTM D 1238
FLAME CHARACTERISTICS Value Unit Standard
FAA Flammability, FAR 25.853 A/B SECT A-1 - FAR 25.853
OSU total heat release (2 minute test) 5 kW-min/m² FAR 25.853
OSU peak heat release rate (5 minute test) 40 kW/m² FAR 25.853
Vertical Burn a (60s) passes at 5 sec FAR 25.853
Vertical Burn b (12s) passes at 0 sec FAR 25.853
Source GMD, last updated:01/13/2000

Processing

Parameter
Injection Molding Value Unit
Drying Temperature 135 °C
Drying Time 4 - 6 hrs
Drying Time (Cumulative) 24 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 340 - 360 °C
Nozzle Temperature 330 - 355 °C
Front - Zone 3 Temperature 340 - 360 °C
Middle - Zone 2 Temperature 325 - 350 °C
Rear - Zone 1 Temperature 315 - 340 °C
Mold Temperature 135 - 165 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 40 - 70 rpm
Shot to Cylinder Size 40 - 60 %
Vent Depth 0.025 - 0.076 mm
Source GMD, last updated:01/13/2000


For more information please download the datasheet
S-Plastic Ultem 9070 High Flow Polyetherimide Blend S-Plastics Ultem 9070.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

S-Plastic Ultem 9070 High Flow Polyetherimide BlendClick to consult and get the latest quotation within 24 hours!

S-Plastic Ultem 9070 High Flow Polyetherimide Blend


Product Tags:

High Flow

      

ECO Conforming

      
Wholesale S-Plastic Ultem 9070 High Flow Polyetherimide Blend from china suppliers

S-Plastic Ultem 9070 High Flow Polyetherimide Blend Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: SAMTION INTERNATIONAL LIMITED
*Subject:
*Message:
Characters Remaining: (0/3000)
 
You May Like