S-Plastic Stat-kon OEL32 a compound based on PPS (linear-based) containing carbon fiber and PTFE.

Name: SPlastic Statkon OEL32 a compound based on PPS linearbased containing carbon fiber and PTFE
Brand: S-Plastic Stat-kon
Price: 1 USD

Wholesale S-Plastic Stat-kon OEL32 a compound based on PPS (linear-based) containing carbon fiber and PTFE. from china suppliers

Brand Name : S-Plastic Stat-kon

Model Number : OEL32

Certification : COA/ICP Test/Rohs/MSDS

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Stat-kon OEL32 resin is a compound based on PPS (linear-based) containing carbon fiber and PTFE.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	132	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	132	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	1.6	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	1.6	%	ASTM D 638
Tensile Modulus, 50 mm/min	12560	MPa	ASTM D 638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	1	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	9200	MPa	ASTM D 790
Tensile Stress, yield, 5 mm/min	127	MPa	ISO 527
Tensile Stress, break, 5 mm/min	127	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	1.4	%	ISO 527
Tensile Strain, break, 5 mm/min	1.4	%	ISO 527
Tensile Modulus, 1 mm/min	10500	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	119	MPa	ISO 178
Flexural Strain, break, 2 mm/min	119	%	ISO 178
Flexural Modulus, 2 mm/min	9180	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	345	J/m	ASTM D 4812
Izod Impact, notched, 23°C	38	J/m	ASTM D 256
Izod Impact, unnotched 80104 +23°C	21	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	3	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	274	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	247	°C	ASTM D 648
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	274	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	234	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.44	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.02	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	0.2 - 0.5	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	0.7 - 0.9	%	ASTM D 955
Density	1.44	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.03	%	ISO 62
ELECTRICAL	Value	Unit	Standard
Surface Resistivity	2.E+00 - 4.E+00	Ohm	ASTM D 257
Source GMD, last updated:03/26/2008

Processing

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.

Other related products we recommend:

For more information please download the datesheet
	S-Plastics Stat-kon OEL32.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!