S-Plastic Stat-kon MS000IL a compound based on Polypropylene resin containing Stainless Steel. Added features of this materi

Name: SPlastic Statkon MS000IL a compound based on Polypropylene resin containing Stainless Steel Added features of this materi
Brand: S-Plastic Stat-kon
Price: 1 USD

Wholesale S-Plastic Stat-kon MS000IL a compound based on Polypropylene resin containing Stainless Steel. Added features of this materi from china suppliers

Brand Name : S-Plastic Stat-kon

Model Number : MS000IL

Certification : COA/ICP Test/Rohs/MSDS

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Stat-kon MS000IL resin is a compound based on Polypropylene resin containing Stainless Steel. Added features of this material include:

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yield	21	MPa	ASTM D 638
Tensile Stress, break	15	MPa	ASTM D 638
Tensile Strain, yield	7.1	%	ASTM D 638
Tensile Strain, break	76	%	ASTM D 638
Tensile Modulus, 50 mm/min	1260	MPa	ASTM D 638
Flexural Stress	27	MPa	ASTM D 790
Flexural Modulus	1270	MPa	ASTM D 790
Tensile Stress, yield	20	MPa	ISO 527
Tensile Stress, break	16	MPa	ISO 527
Tensile Strain, yield	5.6	%	ISO 527
Tensile Strain, break	38.9	%	ISO 527
Tensile Modulus, 1 mm/min	1170	MPa	ISO 527
Flexural Stress	24	MPa	ISO 178
Flexural Modulus	1180	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	1329	J/m	ASTM D 4812
Izod Impact, notched, 23°C	96	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	10	J	ASTM D 3763
Multiaxial Impact	9	J	ISO 6603
Izod Impact, unnotched 80104 +23°C	NB	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	10	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 1.82 MPa, 3.2mm, unannealed	52	°C	ASTM D 648
CTE, -40°C to 40°C, flow	9.9E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	1.17E-04	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	1.01E-04	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	1.17E-04	1/°C	ISO 11359-2
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	52	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	0.96	g/cm³	ASTM D 792
Mold Shrinkage, flow, 24 hrs	1.3	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	1.4	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	1.29	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	1.38	%	ISO 294
Density	0.96	g/cm³	ISO 1183
ELECTRICAL	Value	Unit	Standard
Surface Resistivity	1.E+02 - 1.E+06	Ohm	ASTM D 257
Source GMD, last updated:09/24/2008

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Melt Temperature	225 - 250	°C
Front - Zone 3 Temperature	240 - 250	°C
Middle - Zone 2 Temperature	215 - 225	°C
Rear - Zone 1 Temperature	195 - 205	°C
Mold Temperature	30 - 50	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:09/24/2008

Other related products we recommend:

For more information please download the datesheet
	S-Plastics Stat-kon MS000IL.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!