S-Plastic Thermocomp LC008EXP is a compound based on Polyetheretherketone containing Carbon Fiber. Added features include

Product Categories

Valox Plastic [1]
Ultem PEI Resin [197]
Cycoloy PC ABS [9]
Xenoy Resin [2]
Cycolac ABS [173]
Geloy Resin [110]
Colorcomp [20]
LNP Faradex [37]
S-Plastic Lubricomp [506]
LNP Stat Kon [308]
S-Plastic Thermocomp [705]
Plastic Resin Pellets Bulk [113]
Verton Plastic [106]

SAMTION INTERNATIONAL LIMITED

Contact Now

S-Plastic Thermocomp LC008EXP is a compound based on Polyetheretherketone containing Carbon Fiber. Added features include

Name: SPlastic Thermocomp LC008EXP is a compound based on Polyetheretherketone containing Carbon Fiber Added features include
Brand: S-Plastic Thermocomp
Price: 1 USD

Wholesale S-Plastic Thermocomp LC008EXP is a compound based on Polyetheretherketone containing Carbon Fiber. Added features include from china suppliers

Brand Name : S-Plastic Thermocomp

Model Number : LC008EXP

Certification : Datasheet，MSDS，ROHS，SGS，REACH，FDA，EU，UL，COC/COA ,please contact us

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Thermocomp LC008EXP resin is a compound based on Polyetheretherketone containing Carbon Fiber. Added features include

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, break, 5 mm/min	256	MPa	ISO 527
Tensile Strain, break, 5 mm/min	1.6	%	ISO 527
Tensile Modulus, 1 mm/min	26200	MPa	ISO 527
Flexural Stress, break, 2 mm/min	341	MPa	ISO 178
Flexural Modulus, 2 mm/min	22900	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched 80104 +23°C	45	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	9	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
CTE, 23°C to 60°C, flow	4.E-06	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	4.1E-05	1/°C	ISO 11359-2
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	>300	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.45	g/cm³	ISO 1183
Source GMD, last updated:11/29/2007

Processing

Injection Molding	Value	Unit
Drying Temperature	120 - 150	°C
Drying Time	4	hrs
Maximum Moisture Content	0.1	%
Melt Temperature	380 - 390	°C
Front - Zone 3 Temperature	380 - 395	°C
Middle - Zone 2 Temperature	365 - 375	°C
Rear - Zone 1 Temperature	350 - 360	°C
Mold Temperature	140 - 165	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	60 - 100	rpm
Source GMD, last updated:11/29/2007
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded
samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.

Other related products we recommend:

For more information please download the datasheet
	S-Plastics Thermocomp LC008EXP.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!

S-Plastic Thermocomp LC008EXP is a compound based on Polyetheretherketone containing Carbon Fiber. Added features include