S-Plastic Thermocomp DF004P compound based on Polycarbonate resin containing Glass Fiber. Added features of this material

Product Categories

Valox Plastic [1]
Ultem PEI Resin [197]
Cycoloy PC ABS [9]
Xenoy Resin [2]
Cycolac ABS [173]
Geloy Resin [110]
Colorcomp [20]
LNP Faradex [37]
S-Plastic Lubricomp [506]
LNP Stat Kon [308]
S-Plastic Thermocomp [705]
Plastic Resin Pellets Bulk [113]
Verton Plastic [106]

SAMTION INTERNATIONAL LIMITED

Contact Now

S-Plastic Thermocomp DF004P compound based on Polycarbonate resin containing Glass Fiber. Added features of this material

Name: SPlastic Thermocomp DF004P compound based on Polycarbonate resin containing Glass Fiber Added features of this material
Brand: S-Plastic Thermocomp
Price: 1 USD

Wholesale S-Plastic Thermocomp DF004P compound based on Polycarbonate resin containing Glass Fiber. Added features of this material from china suppliers

Brand Name : S-Plastic Thermocomp

Model Number : DF004P

Certification : Datasheet，MSDS，ROHS，SGS，REACH，FDA，EU，UL，COC/COA ,please contact us

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Thermocomp DF004P resin is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material
include: Exceptional Processing.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, break	104	MPa	ASTM D 638
Tensile Strain, break	3.2	%	ASTM D 638
Tensile Modulus, 50 mm/min	6190	MPa	ASTM D 638
Flexural Stress	172	MPa	ASTM D 790
Flexural Modulus	6170	MPa	ASTM D 790
Tensile Stress, break	102	MPa	ISO 527
Tensile Strain, break	3.2	%	ISO 527
Tensile Modulus, 1 mm/min	6050	MPa	ISO 527
Flexural Stress	162	MPa	ISO 178
Flexural Modulus	5990	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	710	J/m	ASTM D 4812
Izod Impact, notched, 23°C	74	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	8	J	ASTM D 3763
Multiaxial Impact	2	J	ISO 6603
Izod Impact, unnotched 80104 +23°C	48	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	9	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 1.82 MPa, 3.2mm, unannealed	138	°C	ASTM D 648
CTE, -40°C to 40°C, flow	3.34E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	6.89E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	3.35E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	5.45E-05	1/°C	ISO 11359-2
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	139	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Moisture Absorption, 50% RH, 24 hrs	0.12	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	0.2	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	0.7	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	0.23	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.67	%	ISO 294
Moisture Absorption (23°C / 50% RH)	0.19	%	ISO 62
Source GMD, last updated:09/27/2004

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120	°C
Drying Time	4	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	305 - 325	°C
Front - Zone 3 Temperature	320 - 330	°C
Middle - Zone 2 Temperature	310 - 320	°C
Rear - Zone 1 Temperature	295 - 305	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:09/27/2004

Other related products we recommend:

For more information please download the datasheet
	S-Plastics Thermocomp DF004P.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!

S-Plastic Thermocomp DF004P compound based on Polycarbonate resin containing Glass Fiber. Added features of this material